Brass has a muted yellow color, somewhat similar to gold. It is relatively resistant to tarnishing, and is often used as decoration and for coins. In antiquity, polished brass was often used as a mirror.

Brass has likely been known to humans since prehistoric times, even before zinc itself was discovered. It was produced by melting copper together with calamine, a zinc ore. In the German village of Breinigerberg, an ancient Roman settlement was discovered where a calamine ore mine existed. During the melting process, the zinc is extracted from the calamine and mixes with the copper. Pure zinc, on the other hand, has too low a boiling point to have been produced by ancient metalworking techniques. The many references to 'brass' appearing throughout the King James Bible are thought to signify another bronze alloy, or copper, rather than the strict modern definition of 'brass'.

Properties

Brass has higher malleability than copper or zinc. The relatively low melting point of brass (900 to 940°C, depending on composition) and its flow characteristics make it a relatively easy material to cast. By varying the proportions of copper and zinc, the properties of the brass can be changed, allowing hard and soft brasses. The density of brass is approximately 8400 to 8730 kilograms per cubic metre (equivalent to 8.4 to 8.73 grams per cubic centimetre).

Today almost 90%Fact: date=November 2008 of all brass alloys are recycled. Because brass is not ferromagnetic, it can be separated from ferrous scrap by passing the scrap near a powerful magnet. Brass scrap is collected and transported to the foundry where it is melted and recast into billets. Billets are heated and extruded into the desired form and size.

Aluminium makes brass stronger and more corrosion resistant. Aluminium also causes a highly beneficial hard layer of aluminium oxide (Al₂O₃) to be formed on the surface that is thin, transparent and self healing. Tin has a similar effect and finds its use especially in sea water applications (naval brasses). Combinations of iron, aluminium, silicon and manganese make brass wear and tear resistant. A well known alloy used in the automotive industry is 'LDM C673', where the combination of manganese and silicon leads to a strong and resistant brass.

Applications

The so called dezincification resistant (DZR) brasses, like alloy 'LDM G563' (known for its brand name 'Enkotal'), are used where there is a large corrosion risk and where normal brasses do not meet the standards. Applications with high water temperatures, chlorides present or deviating water qualities (soft water) play a role. DZR-brass is excellent in water boiler systems. This brass alloy must be produced with great care, with special attention placed on a balanced composition and proper production temperatures and parameters to avoid long-term failures.